ASTM_A_562_-_A_562M_-_10_2015.pdf

Designation:A562/A562M10(Reapproved 2015)Standard Specification forPressure Vessel Plates,Carbon Steel,Manganese-Titaniumfor Glass or Diffused Metallic Coatings1This standard is issued under the fixed designation A562/A562M;the number immediately following the designation indicates the yearof original adoption or,in the case of revision,the year of last revision.A number in parentheses indicates the year of last reapproval.A superscript epsilon()indicates an editorial change since the last revision or reapproval.1.Scope1.1 This specification2covers titanium-bearing carbon steelplates intended for welded glass lined pressure vessels or otherapplications where the presence of free-iron carbide would bedeleterious to the coating.Aminimum specific ratio of titaniumto carbon is specified.1.2 The maximum thickness of plates is limited to 2 in.50mm.1.3 The values stated in either inch-pound units or SI unitsare to be regarded separately as standard.Within the text,theSI units are shown in brackets.The values stated in eachsystem are not exact equivalents;therefore,each system mustbe used independently of the other.Combining values from thetwo systems may result in nonconformance with the specifi-cation.2.Referenced Documents2.1 ASTM Standards:3A20/A20M Specification for General Requirements for SteelPlates for Pressure Vessels3.General Requirements and Ordering Information3.1 Material supplied to this material specification shallconform to Specification A20/A20M.These requirements out-line the testing and retesting methods and procedures,permit-ted variations in dimensions,and mass,quality and repair ofdefects,marking,loading,and ordering information.3.2 Inadditiontothebasicrequirementsofthisspecification,certain supplementary requirements are availablewhen additional control,testing,or examination is required tomeet end use requirements.3.3 If the requirements of this specification are in conflictwith the requirements of Specification A20/A20M,the require-ments of this specification shall prevail.4.Manufacture4.1 Steelmaking PracticeThe steel shall be killed.5.Heat Treatment5.1 Plates shall be thermally treated to produce grainrefinement,either by normalizing or heating uniformly for hotforming at a minimum temperature of 1600F 870C or somehigher agreed temperature,and held at this temperature for aminimum of 1 h/in.2.4 min/mm of thickness.6.Chemical Requirements6.1 The steel shall conform to the chemical requirementsshown in Table 1 unless otherwise modified in accordance withSupplementary Requirement S17,Vacuum Carbon-DeoxidizedSteel,in Specification A20/A20M.7.Mechanical Requirements7.1 Tension Test RequirementsThe material as representedby the tension-test specimens shall conform to the require-ments shown in Table 2.1This specification is under the jurisdiction of ASTM Committee A01 on Steel,Stainless Steel and Related Alloys and is the direct responsibility of SubcommitteeA01.11 on Steel Plates for Boilers and Pressure Vessels.Current edition approved Sept.1,2015.Published September 2015.Originallyapproved in 1966.Last previous edition approved in 2010 as A562/A562M 10.DOI:10.1520/A0562_A0562M-10R15.2For ASME Boiler and Pressure Vessel Code applications,see related Specifi-cation SA-562/SA-562M in Section II of that Code.3For referenced ASTM standards,visit the ASTM website,www.astm.org,orcontact ASTM Customer Service at serviceastm.org.For Annual Book of ASTMStandards volume information,refer to the standards Document Summary page onthe ASTM website.Copyright ASTM International,100 Barr Harbor Drive,PO Box C700,West Conshohocken,PA 19428-2959.United States1 SUPPLEMENTARY REQUIREMENTSSupplementary requirements shall not apply unless specified in the order.Alist of standardized supplementary requirements for use at the option of the purchaser are includedin Specification A20/A20M.Those which are considered suitable for use with this specification arelisted below by title.S1.Vacuum Treatment,S2.Product Analysis,S3.Simulated Post-Weld Heat Treatment of MechanicalTest Coupons,S4.Additional Tension Test,S5.Charpy V-Notch Impact Test,S6.Drop Weight Test(for Material 0.625 in.16 mm andover in Thickness),S7.High-temperature Tension Test,S8.Ultrasonic Examination in accordance with Specifica-tion A435/A435M,S9.Magnetic Particle Examination,S11.Ultrasonic Examination in accordance with Specifica-tion A577/A577M,S12.Ultrasonic Examination in accordance with Specifica-tion A578/A578M,andS17.Vacuum Carbon-Deoxidized Steel.ASTM International takes no position respecting the validity of any patent rights asserted in connection with any item mentionedin this standard.Users of this standard are expressly advised that determination of the validity of any such patent rights,and the riskof infringement of such rights,are entirely their own responsibility.This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years andif not revised,either reapproved or withdrawn.