ASTM_A_1010_-_A_1010M_-_13.pdf

Designation:A1010/A1010M13Standard Specification forHigher-Strength Martensitic Stainless Steel Plate,Sheet,andStrip1This standard is issued under the fixed designation A1010/A1010M;the number immediately following the designation indicates theyear of original adoption or,in the case of revision,the year of last revision.A number in parentheses indicates the year of lastreapproval.A superscript epsilon()indicates an editorial change since the last revision or reapproval.1.Scope*1.1 This specification covers martensitic stainless steels forvarious structural,architectural,pressure vessel,and heat-resisting applications.The mechanical properties of thesesteels are customarily,but not necessarily,developed by asuitable heat treatment generally referred to as tempering.1.2 Steel products under this specification are available intwo grades:GradeYield Strength,min,ksi MPa40 27540 27550 34550 3451.3 The maximum thickness of plates is limited only by thecapacity of the composition to meet the specified mechanicalproperty requirements;however,current practice normallylimits the maximum thickness of plates furnished under thisspecification to 2 in.50 mm.1.4 The values stated in either SI units or inch-pound unitsare to be regarded separately as standard.The values stated ineach system may not be exact equivalents;therefore,eachsystem shall be used independently of the other.Combiningvalues from the two systems may result in non-conformancewith the standard.2.Referenced Documents2.1 ASTM Standards:2A480/A480M Specification for General Requirements forFlat-Rolled Stainless and Heat-Resisting Steel Plate,Sheet,and StripA673/A673M Specification for Sampling Procedure for Im-pact Testing of Structural SteelE527 Practice for Numbering Metals and Alloys in theUnified Numbering System(UNS)2.2 Other Document:SAE J1086 Recommended Practice for Numbering Metalsand Alloys33.General Requirements3.1 The following requirements for orders for materialfurnished under this specification shall conform to the appli-cable requirements of the current edition of SpecificationA480/A480M.3.1.1 Terminology,3.1.2 Ordering Information,3.1.3 Process,3.1.4 Heat Analysis,3.1.5 Product Analysis,3.1.6 Finish for Sheet,3.1.7 Finish for Strip,3.1.8 Finish for Plates,3.1.9 Test Specimens,3.1.10 Number of Tests,3.1.11 Test Methods,3.1.12 Retests and Retreatment,3.1.13 Dimensions and Permissible Variations,3.1.14 Workmanship,3.1.15 Packaging,Marking,and Loading,3.1.16 Inspection,3.1.17 Rejection and Rehearing,and3.1.18 Material Test Report and Certification.4.Chemical Composition4.1 The steel shall conform to the requirements as tochemical composition specified in Table 1,and shall conformto applicable requirements specified in the current edition ofSpecification A480/A480M.5.Heat Treatment5.1 The material shall be heat-treated by tempering to meetthe requirements of this specification.The tempering tempera-ture shall not exceed 1400F 760C.Prior to tempering,thesteel shall be in the as-rolled,normalized or quenched condi-tion.1This specification is under the jurisdiction of ASTM Committee A01 on Steel,Stainless Steel and Related Alloys and is the direct responsibility of SubcommitteeA01.17 on Flat-Rolled and Wrought Stainless Steel.Current edition approved Oct.1,2013.Published October 2013.Originallyapproved in 2000.Last previous edition approved in 2009 as A1010/A1010M 01(2009).DOI:10.1520/A1010_A1010M-13.2For referenced ASTM standards,visit the ASTM website,www.astm.org,orcontact ASTM Customer Service at serviceastm.org.For Annual Book of ASTMStandards volume information,refer to the standards Document Summary page onthe ASTM website.3Available from Society of Automotive Engineers(SAE),400 CommonwealthDr.,Warrendale,PA 15096-0001,http:/www.sae.org.*A Summary of Changes section appears at the end of this standardCopyright ASTM International,100 Barr Harbor Drive,PO Box C700,West Conshohocken,PA 19428-2959.United States1Copyright by ASTM Intl(all rights reserved);6.Mechanical Properties6.1 The material shall conform to the mechanical propertiesspecified in Table 2.7.Keywords7.1 architectural steel;martensitic;plate;stainless steel;steel;structural steel;temperedSUPPLEMENTARY REQUIREMENTSSupplementary requirements shall not apply unless specified on the purchase order.Requirementsother than those shown in this section may be specified subject to agreement between the supplier andthe purchaser.The following supplementary requirements are suitable for use with this specification.S1.Charpy V-Notch Impact TestS1.1 Charpy V-notch impact tests shall be conducted inaccordance with Specification A673/A673M.S1.2 The frequency of testing,the test temperature to beused,and the absorbed energy requirements shall be asspecified on the order.S2.Ultrasonic ExaminationS2.1 The material shall be ultrasonically examined in ac-cordance with the requirements specified on the order.SUMMARY OF CHANGESCommittee A01 has identified the location of selected changes to this standar