温馨提示:
1. 部分包含数学公式或PPT动画的文件,查看预览时可能会显示错乱或异常,文件下载后无此问题,请放心下载。
2. 本文档由用户上传,版权归属用户,汇文网负责整理代发布。如果您对本文档版权有争议请及时联系客服。
3. 下载前请仔细阅读文档内容,确认文档内容符合您的需求后进行下载,若出现内容与标题不符可向本站投诉处理。
4. 下载文档时可能由于网络波动等原因无法下载或下载错误,付费完成后未能成功下载的用户请联系客服处理。
网站客服:3074922707
TM_C_647_
_08_2013
Designation:C64708(Reapproved 2013)Standard Guide toProperties and Tests of Mastics and Coating Finishes forThermal Insulation1This standard is issued under the fixed designation C647;the number immediately following the designation indicates the year oforiginal adoption or,in the case of revision,the year of last revision.A number in parentheses indicates the year of last reapproval.Asuperscript epsilon()indicates an editorial change since the last revision or reapproval.1.Scope1.1 This guide identifies properties of mastics and coatingfinishes characterizing their performance as finishes for ther-mal insulation.1.2 These properties relate to application and service.Eachproperty is defined,and its significance and suggested testmethods are described.1.3 The properties appear in the following order in thisguide.ParagraphApplication Properties6Consistency6.1Coverage6.2Build6.3Wet Flammability6.4Toxicity6.5Temperature and Humidity Range6.6Surface Wetting and Adhesion6.7Gap Filling and Bridging6.8Sizing and Sealing6.9Corrosion or Solvent Attack6.10Drying Time and Curing Time6.11Shrinkage6.12Storage Stability6.13Freeze-Thaw Stability6.14Service Properties7Specimen Preparation7.1Outdoor Durability7.2Environmental Resistance7.3Temperature Limits7.3.1Chemicals and Water Resistance7.3.2Mold and Mildew Resistance7.3.3Surface Flammability7.4Water-Vapor Transmission Rate7.5Adhesion7.6Damage Resistance7.7Impact Resistance7.7.1Abrasion Resistance7.7.2Stress Resistance7.8Flexure7.8.1Elongation7.8.2Color7.9Odor7.10Other Properties81.4 The values stated in inch-pound units are to be regardedas standard.The values given in parentheses are mathematicalconversions to SI units that are provided for information onlyand are not considered standard.2.Referenced Documents2.1 ASTM Standards:2C168 Terminology Relating to Thermal InsulationC419 Practice for Making and Curing Test Specimens ofMastic Thermal Insulation CoatingsC461 Test Methods for Mastics and Coatings Used WithThermal InsulationC488 Test Method for Conducting Exterior Exposure Testsof Finishes for Thermal InsulationC639 Test Method for Rheological(Flow)Properties ofElastomeric SealantsC681 Test Method for Volatility of Oil-and Resin-Based,Knife-Grade,Channel Glazing CompoundsC733 Test Method for Volume Shrinkage of Latex Sealants(Withdrawn 2000)3C755 Practice for Selection of Water Vapor Retarders forThermal InsulationC792 Test Method for Effects of HeatAging on Weight Loss,Cracking,and Chalking of Elastomeric SealantsD36/D36M Test Method for Softening Point of Bitumen(Ring-and-Ball Apparatus)D56 Test Method for Flash Point by Tag Closed Cup TesterD92 Test Method for Flash and Fire Points by ClevelandOpen Cup TesterD93 Test Methods for Flash Point by Pensky-MartensClosed Cup TesterD529 Practice for Enclosed Carbon-Arc Exposures of Bitu-minous Materials(Withdrawn 2013)3D543 Practices for Evaluating the Resistance of Plastics toChemical Reagents1This guide is under the jurisdiction of ASTM Committee C16 on ThermalInsulation and is the direct responsibility of Subcommittee C16.33 on InsulationFinishes and Moisture.Current edition approved Nov.1,2013.Published January 2014.Originallyapproved in 1969.Last previous edition approved in 2008 as C647 08).DOI:10.1520/C0647-08R13.2For referenced ASTM standards,visit the ASTM website,www.astm.org,orcontact ASTM Customer Service at serviceastm.org.For Annual Book of ASTMStandards volume information,refer to the standards Document Summary page onthe ASTM website.3The last approved version of this historical standard is referenced onwww.astm.org.Copyright ASTM International,100 Barr Harbor Drive,PO Box C700,West Conshohocken,PA 19428-2959.United States1 D562 Test Method for Consistency of Paints MeasuringKrebs Unit(KU)Viscosity Using a Stormer-Type Viscom-eterD638 Test Method for Tensile Properties of PlasticsD658 Test Method for Abrasion Resistance of OrganicCoatings by Air Blast Abrasive(Withdrawn 1996)3D747 Test Method for Apparent Bending Modulus of Plas-tics by Means of a Cantilever BeamD790 Test Methods for Flexural Properties of Unreinforcedand Reinforced Plastics and Electrical Insulating Materi-alsD822/D822M Practice for Filtered Open-Flame Carbon-ArcExposures of Paint and Related CoatingsD903 Test Method for Peel or Stripping Strength of Adhe-sive BondsD968 Test Methods for Abrasion Resistance of OrganicCoatings by Falling AbrasiveD1310 Test Method for Flash Point and Fire Point of Liquidsby Tag Open-Cup ApparatusD1640 Test Methods for Drying,Curing,or Film Formationof Organic Coatings at Room TemperatureD1654 Test Method for Evaluation of Painted or CoatedSpecimens Subjected to Corrosive EnvironmentsD1729 Practice for Visual Appraisal of Colors and ColorDifferences of Diffusely-Illuminated Opaque MaterialsD1823 Test Method for Apparent Viscosity of Plastisols andOrganosols at High Shear Rates by Extrusion ViscometerD1824 Test Method for Apparent Viscosity of Plastisols andOrganosols at Low Shear RatesD1849 Test Method for