温馨提示:
1. 部分包含数学公式或PPT动画的文件,查看预览时可能会显示错乱或异常,文件下载后无此问题,请放心下载。
2. 本文档由用户上传,版权归属用户,汇文网负责整理代发布。如果您对本文档版权有争议请及时联系客服。
3. 下载前请仔细阅读文档内容,确认文档内容符合您的需求后进行下载,若出现内容与标题不符可向本站投诉处理。
4. 下载文档时可能由于网络波动等原因无法下载或下载错误,付费完成后未能成功下载的用户请联系客服处理。
网站客服:3074922707
TM_D_2048_
_17
Designation:D204817Standard Test Method forPowdering of Floor Polish Films1This standard is issued under the fixed designation D2048;the number immediately following the designation indicates the year oforiginal adoption or,in the case of revision,the year of last revision.A number in parentheses indicates the year of last reapproval.Asuperscript epsilon()indicates an editorial change since the last revision or reapproval.1.Scope1.1 This test method covers a bench procedure for thedetermination of the degree of powdering of floor polishesunder ambient conditions as well as conditions of low relativehumidity.1.2 The values stated in inch-pound units are to be regardedas standard.The values given in parentheses are mathematicalconversions to SI units that are provided for information onlyand are not considered standard.1.3 This standard does not purport to address all of thesafety concerns,if any,associated with its use.It is theresponsibility of the user of this standard to establish appro-priate safety and health practices and determine the applica-bility of regulatory limitations prior to use.1.4 This international standard was developed in accor-dance with internationally recognized principles on standard-ization established in the Decision on Principles for theDevelopment of International Standards,Guides and Recom-mendations issued by the World Trade Organization TechnicalBarriers to Trade(TBT)Committee.2.Referenced Documents2.1 ASTM Standards:2D3153 Test Method for Recoatability of Water-EmulsionFloor Polishes3.Terminology3.1 Definitions:3.1.1 powderingpartial or total disintegration of the polishfilm resulting in a fine,light colored material.4.Significance and Use4.1 This is a comparative test method.If this method doesnot indicate powdering,it is still possible that the product inactual use may powder.5.Apparatus5.1 Textile Crockmeter,3weighted with a 2.2-lb(1-kg)weight.The weight is placed directly over the abrasion doweland attached with two-faced tape.5.2 Abrading Felt670 Kelly No.720 billiard cloth cut into2 by 2-in.(50 by 50-mm)squares.5.3 SubstrateOfficial Vinyl Composition Tile(OVCT)4shall be used in this test.5.4 Volumetric Pipet,0.07-oz(2-mL).5.5 Cheesecloth Applicator,washed to remove sizing;cutinto 2-in.(50-mm)strips of four-ply cloth;folded twice.5.6 Relative Humidity and Temperature Indicator.5.7 Glove BoxAn enclosure that houses the crockmeterkeeping it in a constant humidity and temperature environment;features rubber glove inserts so that the tests may be runkeeping the environment of the crockmeter constant.5.8 DesiccantSilica gel or calcium chloride.5.9 Salts for Constant Humidity ConditionsLiClH2O,CaCl26H2O,or Mg(NO3)26H2O.NOTE1Saturated aqueous solutions of the following salts in contactwith an excess of a definite solid phase of salt at the indicatedtemperatures and in an enclosed space will maintain the required constanthumidities:LiClH2O at 77F(25C)yields 11.1%relative humidity.CaCl26H2O at 50F(10C)yields 38.0%relative humidity.Mg(NO3)26H2O at 75F(23.9C)yields 42.9%relative humidity.5.10 Fan,small,electric.5.11 Metal Clip,to hold the abrading felt on the crockmetersurface during testing.1This test method is under the jurisdiction ofASTM Committee D21 on Polishesand is the responsibility of Subcommittee D21.04 on Performance Tests.Current edition approved March 1,2017.Published April 2017.Originallyapproved in 1964.Last previous edition approved in 2010 as D2048 10.DOI:10.1520/D2048-17.2For referenced ASTM standards,visit the ASTM website,www.astm.org,orcontact ASTM Customer Service at serviceastm.org.For Annual Book of ASTMStandards volume information,refer to the standards Document Summary page onthe ASTM website.3The sole source of supply of the apparatus known to the committee at this timeis Atlas Electric Devices Co.,Chicago,IL.If you are aware of alternative suppliers,please provide this information toASTM Headquarters.Your comments will receivecareful consideration at a meeting of the responsible technical committee,whichyou may attend.4OVCT tile may be obtained through Armstrong Flooring from various homeimprovement stores.The following Armstrong tile substrates have been found toperform adequately for this test method:Armstrong Excelon Feature Tile:Black(56790),http:/ ASTM International,100 Barr Harbor Drive,PO Box C700,West Conshohocken,PA 19428-2959.United StatesThis international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for theDevelopment of International Standards,Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade(TBT)Committee.1 6.Preparation of Test Sample6.1 Clean the tile surface in accordance with Test MethodD3153,paragraph 9.1.2,to ensure removal of any coatingpresent.6.2 Pipet 0.07 oz(2 mL)of polish onto the center of the testpanel.Place the cheesecloth into the polish and allow it toabsorb the emulsion.Distribute the