ASTM_D_2105_-_01_2019.pdf

Designation:D210501(Reapproved 2019)Standard Test Method forLongitudinal Tensile Properties of“Fiberglass”(Glass-Fiber-Reinforced Thermosetting-Resin)Pipe and Tube1This standard is issued under the fixed designation D2105;the number immediately following the designation indicates the year oforiginal adoption or,in the case of revision,the year of last revision.A number in parentheses indicates the year of last reapproval.Asuperscript epsilon()indicates an editorial change since the last revision or reapproval.1.Scope1.1 This test method covers the determination of the com-parative longitudinal tensile properties of fiberglass pipe whentested under defined conditions of pretreatment,temperature,and testing machine speed.Both glass-fiber-reinforcedthermosetting-resin pipe(RTRP)and glass-fiber-reinforcedpolymer mortar pipe(RPMP)are fiberglass pipes.NOTE1For the purposes of this standard,polymer does not includenatural polymer.1.2 This test method is generally limited to pipe diameter of6 in.(150 mm)or smaller.Larger sizes may be tested ifrequired apparatus is available.1.3 The values stated in inch-pound units are to be regardedas the standard.The values given in parentheses are providedfor information purposes only.1.4 This standard does not purport to address all of thesafety concerns,if any,associated with its use.It is theresponsibility of the user of this standard to establish appro-priate safety,health,and environmental practices and deter-mine the applicability of regulatory limitations prior to use.NOTE2There is no known ISO equivalent to this standard.1.5 This international standard was developed in accor-dance with internationally recognized principles on standard-ization established in the Decision on Principles for theDevelopment of International Standards,Guides and Recom-mendations issued by the World Trade Organization TechnicalBarriers to Trade(TBT)Committee.2.Referenced Documents2.1 ASTM Standards:2C33 Specification for Concrete AggregatesD618 Practice for Conditioning Plastics for TestingD638 Test Method for Tensile Properties of PlasticsD638M Test Method for Tensile Properties of Plastics(Met-ric)(Withdrawn 1996)3D883 Terminology Relating to PlasticsD1600 Terminology forAbbreviated Terms Relating to Plas-ticsD3567 Practice for Determining Dimensions of“Fiberglass”(Glass-Fiber-Reinforced Thermosetting Resin)Pipe andFittingsE4 Practices for Force Verification of Testing MachinesE83 Practice for Verification and Classification of Exten-someter SystemsF412 Terminology Relating to Plastic Piping Systems3.Terminology3.1 GeneralDefinitions are in accordance with Terminol-ogy D883 and F412 and abbreviations are in accordance withTerminology D1600,unless otherwise indicated.3.2 Other definitions of terms and symbols relating totension testing of plastics appear in the Annex to Test MethodsD638 and D638M.3.3 Definitions of Terms Specific to This Standard:3.3.1aggregatea siliceous sand conforming to the re-quirements of Specification C33,except that the requirementsfor gradation shall not apply.3.3.2 exterior surface resin layera resin layer,with orwithout filler or reinforcement,or both,applied to the exteriorsurface of the pipe structural wall.3.3.3 fiberglass pipea tubular product containing glassfiber reinforcement embedded in or surrounded by curedthermosetting resin;the composite structure may containaggregate,granular or platelet fillers,thixotropic agents,pigments,or dyes;thermoplastic or thermosetting liners maybe included.3.3.4linerthe inner portion of the wall at least 0.005 in.(0.13 mm)in thickness,as determined in 9.1.2,which does notcontribute to the strength in the determination of the hydro-static design basis.1This test method is under the jurisdiction of ASTM Committee D20 on Plasticsand is the direct responsibility of Subcommittee D20.23 on Reinforced PlasticPiping Systems and Chemical Equipment.Current edition approved Nov.15,2019.Published December 2019.Originallyapproved in 1962.Last previous edition approved in 2014 as D2105 01(2014).DOI:10.1520/D2105-01R19.2For referenced ASTM standards,visit the ASTM website,www.astm.org,orcontact ASTM Customer Service at serviceastm.org.For Annual Book of ASTMStandards volume information,refer to the standards Document Summary page onthe ASTM website.3The last approved version of this historical standard is referenced onwww.astm.org.*A Summary of Changes section appears at the end of this standardCopyright ASTM International,100 Barr Harbor Drive,PO Box C700,West Conshohocken,PA 19428-2959.United StatesThis international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for theDevelopment of International Standards,Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade(TBT)Committee.13.3.5 reinforced polymer mortar pipe(RPMP)a fiberglasspipe with aggregate.3.3.6 reinforced thermosetting resin pipe(RTRP)a fiber-glass