ASTM_D_3183_-_10_2019.pdf

Designation:D318310(Reapproved 2019)Standard Practice forRubberPreparation of Pieces for Test Purposes fromProducts1This standard is issued under the fixed designation D3183;the number immediately following the designation indicates the year oforiginal adoption or,in the case of revision,the year of last revision.A number in parentheses indicates the year of last reapproval.Asuperscript epsilon()indicates an editorial change since the last revision or reapproval.This standard has been approved for use by agencies of the U.S.Department of Defense.1.Scope1.1 This practice covers methods for the preparation ofpieces of a rubber vulcanizate that is not in the form of sheet.Such pieces are used as a source from which specimens areobtained for testing.1.2 The values stated in SI units are to be regarded as thestandard.The values given in parentheses are for informationonly.1.3 This standard does not purport to address all of thesafety concerns,if any,associated with its use.It is theresponsibility of the user of this standard to establish appro-priate safety,health,and environmental practices and deter-mine the applicability of regulatory limitations prior to use.1.4 This international standard was developed in accor-dance with internationally recognized principles on standard-ization established in the Decision on Principles for theDevelopment of International Standards,Guides and Recom-mendations issued by the World Trade Organization TechnicalBarriers to Trade(TBT)Committee.2.Referenced Documents2.1 ASTM Standards:2D3182 Practice for RubberMaterials,Equipment,and Pro-cedures for Mixing Standard Compounds and PreparingStandard Vulcanized Sheets3.Terminology3.1 Definitions of Terms Specific to This Standard:3.1.1 piece,na rubber vulcanizate of a geometry fromwhich a specimen,suitable for testing,may be obtained.4.Significance and Use4.1 This practice is used when it is necessary to test aproduct from which specimens cannot be cut directly.Proce-dures are given for preparing pieces suitable for preparingspecimens of the product.5.Conditioning5.1 Pieces shall be prepared for specimen cutting and testingnot sooner than 16 h after vulcanization and not later than 60days after delivery to a purchaser(Note 1).5.2 Testing,for the purpose of production control,mayrequire that the pieces be prepared and tested prior to 16 h asspecified in 5.1.This practice shall be noted in the respectivetest report.NOTE1This procedures time limit may be modified as agreed uponbetween laboratories or between supplier and user.6.Pieces6.1 Pieces shall be obtained,if possible,from the product tobe tested in accordance with the specification for the particularproduct.The pieces shall be prepared in accordance withSection 7.6.2 When it is not feasible to prepare suitable pieces fromthe product,specially molded pieces or sheets may be preparedfrom the same unvulcanized rubber compound used to preparethe product.The sheets shall be vulcanized in accordance withPractice D3182 and shall have an equivalent state of vulcani-zation judged from such properties as can be determined on theproduct.The sheets shall have one of the following thicknessesunless another thickness is technically necessary:mmin.2 0.2(0.08 0.008)4 0.2(0.16 0.008)6.3 0.3(0.25 0.12)12.5 0.5(0.50 0.02)7.Preparation of Pieces7.1 Rubber vulcanizates,particularly products,may nothave a suitable form or size for use in cutting specimens fortest.Procedures in this section describe the preparation of1This practice is under the jurisdiction ofASTM Committee D11 on Rubber andRubber-like Materials and is the direct responsibility of Subcommittee D11.10 onPhysical Testing.Current edition approved Nov.1,2019.Published December 2019.Originallyapproved in 1973.Last previous edition approved in 2015 as D3183-10(2015).DOI:10.1520/D3183-10R19.2For referenced ASTM standards,visit the ASTM website,www.astm.org,orcontact ASTM Customer Service at serviceastm.org.For Annual Book of ASTMStandards volume information,refer to the standards Document Summary page onthe ASTM website.Copyright ASTM International,100 Barr Harbor Drive,PO Box C700,West Conshohocken,PA 19428-2959.United StatesThis international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for theDevelopment of International Standards,Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade(TBT)Committee.1 pieces from vulcanizates that are too thick,have unevensurfaces,or contain textiles.7.1.1 After the piece is prepared,it shall rest at least 30 minbefore the specimens are cut.7.2 Separation of TextilesThe separation should prefer-ably avoid the use of a swelling liquid.If this is not possible,use commercial isooctane(2,2,4-trimethylpentane),followingthe safety recommendations from the supplier and the MSDS.7.2.1 Take care to avoid excessive stretching of the rubberduring the separation,by separating a little at