温馨提示:
1. 部分包含数学公式或PPT动画的文件,查看预览时可能会显示错乱或异常,文件下载后无此问题,请放心下载。
2. 本文档由用户上传,版权归属用户,汇文网负责整理代发布。如果您对本文档版权有争议请及时联系客服。
3. 下载前请仔细阅读文档内容,确认文档内容符合您的需求后进行下载,若出现内容与标题不符可向本站投诉处理。
4. 下载文档时可能由于网络波动等原因无法下载或下载错误,付费完成后未能成功下载的用户请联系客服处理。
网站客服:3074922707
TM_D_4848_
_98_2018
Designation:D484898(Reapproved 2018)Standard Terminology Related toForce,Deformation and Related Properties of Textiles1This standard is issued under the fixed designation D4848;the number immediately following the designation indicates the year oforiginal adoption or,in the case of revision,the year of last revision.A number in parentheses indicates the year of last reapproval.Asuperscript epsilon()indicates an editorial change since the last revision or reapproval.1.Scope1.1 This terminology standard is a compilation of defini-tions of technical terms related to force and deformationproperties when evaluating a stress-strain curve of a textile.(See Figs.X1.1 and X1.2.)A chart showing the relationship ofthe basic terms is shown in Table 1.Terms that are generallyunderstood or adequately defined in other readily availablesources are not included.1.2 For other terms associated with textiles,refer to Termi-nology D123.1.3 This international standard was developed in accor-dance with internationally recognized principles on standard-ization established in the Decision on Principles for theDevelopment of International Standards,Guides and Recom-mendations issued by the World Trade Organization TechnicalBarriers to Trade(TBT)Committee.2.Referenced Documents2.1 ASTM Standards:2D123 Terminology Relating to TextilesD1578 Test Method for Breaking Strength of Yarn in SkeinFormD5344 Test Method for Extension Force of Partially Ori-ented Yarn3.Terminologybreak factor,n in yarn testing,the comparative breakingload of a skein of yarn adjusted for the linear density of theyarn expressed in an indirect system.D13.58 D1578breaking elongationSee elongation at break.breaking force,nthe maximum force applied to a materialcarried to rupture.(Compare breaking point,breakingstrength.Syn.force-at-break)DISCUSSIONMaterials that are brittle usually rupture at the maxi-mum force.Materials that are ductile usually experience a maximumforce before rupturing.breaking loaddeprecated term.Use the preferred termbreaking force.breaking point,non a force-elongation curve,or stress-strain curve,the point corresponding with the breaking forceor the breaking stress in a tensile test.(Compare breakingforce.)breaking strength,nstrength expressed in terms of breakingforce.(See also breaking force and strength.Syn.,strengthat break)breaking tenacity,nthe tenacity at the breaking force.(Seealso breaking force,tenacity.)breaking toughness,ntoughness up to the breaking force ofa material.DISCUSSIONBreaking toughness is represented by the area and thestress-strain curve from the origin to the breaking force per unit length,and,in textile strands,is expressed as work(joules)per unit of lineardensity of the material.In textile fabrics,the unit is joules per gram.chord modulus,nin a stress-strain curve,the ratio of thechange in stress to the change in strain between two specifiedpoints on the pression,nthe act,process,or result of compacting,condensing,or pressive force,nthe perpendicular force applied tosurface(s)of a material in pression recovery,nthe degree to which a materialreturns to its original dimension(s)after removal of acompressive pression resistance,nthe ability of a material to opposedeformation under a compressive force.corresponding elongationSee elongation at specified force.corresponding forceSee force-at-specified-elongation.deformation,na change in shape of a material caused byforces of compression,shear,tension,or torsion.DISCUSSIONDeformation may be immediate or delayed.Delayeddeformation may be either recoverable or nonrecoverable.1This terminology is under the jurisdiction ofASTM Committee D13 on Textilesand is the direct responsibility of Subcommittee D13.58 on Yarns and FibersCurrent edition approved Sept.1,2018.Published September 2018.Originallyapproved in 1988.Last previous edition approved in 2012 as D4848 98(2012).DOI:10.1520/D4848-98R18.2For referenced ASTM standards,visit the ASTM website,www.astm.org,orcontact ASTM Customer Service at serviceastm.org.For Annual Book of ASTMStandards volume information,refer to the standards Document Summary page onthe ASTM website.Copyright ASTM International,100 Barr Harbor Drive,PO Box C700,West Conshohocken,PA 19428-2959.United StatesThis international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for theDevelopment of International Standards,Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade(TBT)Committee.1 deformation,permanent,nthe net long-term change in adimension of a specimen after deformation and relaxationunder specified conditions.(Syn.permanent set,nonrecov-erable deformation,and nonrecoverable stretch.DISCUSSIONPermanent deformation is usually expressed as a per-centage of the original dimension.delayed deformation,ndeformation which is time-dependent and exhibited by material subject to a continuingforce.D13.58 D4848elastic limit,nin me