ASTM_D_5329_-_20.pdf

Designation:D532920Standard Test Methods forSealants and Fillers,Hot-Applied,for Joints and Cracks inAsphalt Pavements and Portland Cement ConcretePavements1This standard is issued under the fixed designation D5329;the number immediately following the designation indicates the year oforiginal adoption or,in the case of revision,the year of last revision.A number in parentheses indicates the year of last reapproval.Asuperscript epsilon()indicates an editorial change since the last revision or reapproval.1.Scope1.1 These test methods cover tests for hot-applied types ofjoint and crack sealants and fillers for portland cement concreteand asphaltic concrete pavements.There are numerous stan-dard material specifications that use these test methods.Referto the respective standard material specification of interest todetermine which of the following test methods to use.Forsample melting and concrete block preparation,see theirrespective standard practices.1.2 The test methods appear in the following sections:SectionArtificial Weathering13Asphalt Compatibility12Bond,Non-Immersed8Bond,Water-Immersed9Cone Penetration,Non-Immersed6Flexibility15Flow7Resilience10Resilience,Oven-Aged11Tensile Adhesion141.3 The values stated in SI units are to be regarded asstandard.No other units of measurement are included in thisstandard.1.4 This standard does not purport to address all of thesafety concerns,if any,associated with its use.It is theresponsibility of the user of this standard to establish appro-priate safety,health,and environmental practices and deter-mine the applicability of regulatory limitations prior to use.1.5 This international standard was developed in accor-dance with internationally recognized principles on standard-ization established in the Decision on Principles for theDevelopment of International Standards,Guides and Recom-mendations issued by the World Trade Organization TechnicalBarriers to Trade(TBT)Committee.2.Referenced Documents2.1 ASTM Standards:2D5/D5M Test Method for Penetration of Bituminous Mate-rialsD217 Test Methods for Cone Penetration of LubricatingGreaseD618 Practice for Conditioning Plastics for TestingD1074 Test Method for Compressive Strength of AsphaltMixturesD1561/D1561M Practice for Preparation of BituminousMixture Test Specimens by Means of California KneadingCompactorD1985 Practice for Preparing Concrete Blocks for TestingSealants,for Joints and CracksD3381/D3381M Specification for Viscosity-Graded AsphaltBinder for Use in Pavement ConstructionD5167 Practice for Melting of Hot-Applied Joint and CrackSealant and Filler for EvaluationD6690 Specification for Joint and Crack Sealants,HotApplied,for Concrete and Asphalt PavementsE145 Specification for Gravity-Convection and Forced-Ventilation OvensE177 Practice for Use of the Terms Precision and Bias inASTM Test MethodsE691 Practice for Conducting an Interlaboratory Study toDetermine the Precision of a Test MethodG151 Practice for Exposing Nonmetallic Materials inAccel-erated Test Devices that Use Laboratory Light SourcesG154 Practice for Operating Fluorescent Ultraviolet(UV)Lamp Apparatus for Exposure of Nonmetallic MaterialsG155 Practice for Operating Xenon Arc Light Apparatus forExposure of Non-Metallic Materials3.Significance and Use3.1 These test methods describe procedures for determiningspecification conformance for hot-applied,field-molded jointand crack sealants and fillers.1These test methods are under the jurisdiction of ASTM Committee D04 onRoad and Paving Materials and are the direct responsibility of SubcommitteeD04.33 on Formed In-Place Sealants for Joints and Cracks in Pavements.Current edition approved May 1,2020.Published May 2020.Originallyapproved in 1992.Last previous edition approved in 2016 as D5329 16.DOI:10.1520/D5329-20.2For referenced ASTM standards,visit the ASTM website,www.astm.org,orcontact ASTM Customer Service at serviceastm.org.For Annual Book of ASTMStandards volume information,refer to the standards Document Summary page onthe ASTM website.Copyright ASTM International,100 Barr Harbor Drive,PO Box C700,West Conshohocken,PA 19428-2959.United StatesThis international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for theDevelopment of International Standards,Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade(TBT)Committee.4.Sample Melting4.1 See Practice D5167.5.Standard Conditions5.1 The laboratory atmospheric conditions,hereinafter re-ferred to as standard conditions,shall be in accordance withPractice D618(23 6 2 C,50 6 10%relative humidity).6.Cone Penetration,Non-Immersed6.1 ScopeThis test method covers determination of conepenetration of bituminous joint and crack sealers and fillers.6.2 Significance and UseThe cone penetration,non-immersed is a measure of consistency.Higher values indicatea softer consistency.6.3 ApparatusConduct this test using the apparatus de-sc