温馨提示:
1. 部分包含数学公式或PPT动画的文件,查看预览时可能会显示错乱或异常,文件下载后无此问题,请放心下载。
2. 本文档由用户上传,版权归属用户,汇文网负责整理代发布。如果您对本文档版权有争议请及时联系客服。
3. 下载前请仔细阅读文档内容,确认文档内容符合您的需求后进行下载,若出现内容与标题不符可向本站投诉处理。
4. 下载文档时可能由于网络波动等原因无法下载或下载错误,付费完成后未能成功下载的用户请联系客服处理。
网站客服:3074922707
TM_D_6049_
_03_2017
Designation:D604903(Reapproved 2017)Standard Test Method forRubber PropertyMeasurement of the Viscous and ElasticBehavior of Unvulcanized Raw Rubbers and RubberCompounds by Compression Between Parallel Plates1This standard is issued under the fixed designation D6049;the number immediately following the designation indicates the year oforiginal adoption or,in the case of revision,the year of last revision.A number in parentheses indicates the year of last reapproval.Asuperscript epsilon()indicates an editorial change since the last revision or reapproval.1.Scope1.1 This test method is an adaptation of the GermanStandard DIN 53514,a further development of the former“Defo Test”(see Appendix X1).1.2 This test method is capable of measuring and character-izing the rheological behavior(viscosity and elasticity)ofunvulcanized raw rubbers and rubber compounds,relating tothe macro structure of rubber polymers(average molecularweight,molecular weight distribution,long chain branching,and micro-and macro-gel).1.3 The viscosity and elasticity of unvulcanized rubbers andrubber compounds are determined by subjecting cylindricaltest pieces to a compression/recovery cycle.The dependencyon shear rate at constant shear stress is evaluated and thematerial fatigue behavior is determined in repeat cycle testing.1.4 The non-Newtonian viscous and elastic behavior ofrubbers and rubber compounds can also be evaluated.1.5 Statistical evaluation of the test data provides an indi-cation of data variation,which may be employed as an estimateof the homogeneity of the material tested.1.6 The values stated in SI units are to be regarded as thestandard.The values in parentheses are for information only.1.7 This standard does not purport to address all of thesafety concerns,if any,associated with its use.It is theresponsibility of the user of this standard to establish appro-priate safety,health,and environmental practices and deter-mine the applicability of regulatory limitations prior to use.1.8 This international standard was developed in accor-dance with internationally recognized principles on standard-ization established in the Decision on Principles for theDevelopment of International Standards,Guides and Recom-mendations issued by the World Trade Organization TechnicalBarriers to Trade(TBT)Committee.2.Referenced Documents2.1 ASTM Standards:2D297 Test Methods for Rubber ProductsChemical Analy-sisD926 Test Method for Rubber PropertyPlasticity andRecovery(Parallel Plate Method)D4483 Practice for Evaluating Precision for Test MethodStandards in the Rubber and Carbon Black ManufacturingIndustriesD6048 Practice for Stress Relaxation Testing of RawRubber,Unvulcanized Rubber Compounds,and Thermo-plastic Elastomers2.2 DIN Standards:3DIN 53514 Testing of RubberDetermination of Viscosityand Elasticity Related Numbers of Raw Rubber andRubber Mixes in a Compression Test between ParallelPlatesDIN 53523,Part 1 Testing of Rubber and ElastomersTesting with the Mooney Shearing Disk Viscometer;Preparation of Test Pieces2.3 ISO Standards:4ISO 5725 Precision of Test MethodsDetermination ofRepeatability and Reproducibility for a Standard TestMethod by Interlaboratory TestsISO 7323 RubberRaw and Unvulcanized CompoundedDetermination of Plasticity Number and Recovery Num-ber;Parallel Plate Method3.Terminology3.1 DefinitionsThe following terms appear in logical or-der for the sake of clarity.3.1.1 Multiple Compression Force Testrefer to Section 10for more details.1This test method is under the jurisdiction of Committee D11 on Rubber andRubber-like Materials and is the direct responsibility of Subcommittee D11.12 onProcessability Tests.Current edition approved Oct.1,2017.Published December 2017.Originallyapproved in 1996.Last previous edition approved in 2013 as D6049 03(2013).DOI:10.1520/D6049-03R17.2For referenced ASTM standards,visit the ASTM website,www.astm.org,orcontact ASTM Customer Service at serviceastm.org.For Annual Book of ASTMStandards volume information,refer to the standards Document Summary page onthe ASTM website.3Available from Deutsches Institut fr Normung,Burggrafenstr 6,D10787Berlin 30,Germany.4Available from American National Standards Institute(ANSI),25 W.43rd St.,4th Floor,New York,NY 10036.Copyright ASTM International,100 Barr Harbor Drive,PO Box C700,West Conshohocken,PA 19428-2959.United StatesThis international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for theDevelopment of International Standards,Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade(TBT)Committee.1 3.1.1.1 viscosity number,V10(Ns)the product of the forceF in N required to compress a test piece the final 0.5 mm(0.02in.)in a 6.0 mm(0.24 in.)total compression cycle(from 13.0to 7.0 mm(0.51 to 0.28 in.)and the compression time dt1equaling 10 s.3.1.1.2 total compression time,tTthe time in s required tocompress a test piece the full 6