Designation:D768411(Reapproved 2020)Standard Guide forMicroscopic Characterization of Particles from In-ServiceLubricants1This standard is issued under the fixed designation D7684;the number immediately following the designation indicates the year oforiginal adoption or,in the case of revision,the year of last revision.A number in parentheses indicates the year of last reapproval.Asuperscript epsilon()indicates an editorial change since the last revision or reapproval.1.Scope1.1 This guide covers the classification and reporting ofresults from in-service lubricant particulate debris analysisobtained by microscopic inspection of wear and contaminantparticles extracted from in-service lubricant and hydraulic oilsamples.This guide suggests standardized terminology topromote consistent reporting,provides logical framework todocument likely or possible root causes,and supports inferenceassociated machinery health condition or severity based onavailable debris analysis information.1.2 This guide shall be used in conjunction with an appro-priate wear debris analysis sample preparation and inspectiontechnique including,but not limited to,one of the following:1.2.1 Ferrography using linear glass slides,1.2.2 Ferrography using rotary glass slides,1.2.3 Patch analysis using patch makers(filtration throughmembrane filters),1.2.4 Filter debris analysis,1.2.5 Magnetic plug inspection,or1.2.6 Other means used to extract and inspect particulatedebris from in-service lubricants.1.3 This standard is not intended to evaluate or characterizethe advantage or disadvantage of one or another of theseparticular particle extraction and inspection methods.1.4 The values stated in SI units are to be regarded asstandard.No other units of measurement are included in thisstandard.1.5 This standard does not purport to address all of thesafety concerns,if any,associated with its use.It is theresponsibility of the user of this standard to establish appro-priate safety,health,and environmental practices and deter-mine the applicability of regulatory limitations prior to use.1.6 This international standard was developed in accor-dance with internationally recognized principles on standard-ization established in the Decision on Principles for theDevelopment of International Standards,Guides and Recom-mendations issued by the World Trade Organization TechnicalBarriers to Trade(TBT)Committee.2.Referenced Documents2.1 ASTM Standards:2D4130 Test Method for Sulfate Ion in Brackish Water,Seawater,and BrinesD4175 Terminology Relating to Petroleum Products,LiquidFuels,and LubricantsD7416 Practice for Analysis of In-Service Lubricants Usinga Particular Five-Part(Dielectric Permittivity,Time-Resolved Dielectric Permittivity with Switching MagneticFields,Laser Particle Counter,Microscopic DebrisAnalysis,and Orbital Viscometer)Integrated TesterD7596 Test Method for Automatic Particle Counting andParticle Shape Classification of Oils Using a DirectImaging Integrated TesterD7647 Test Method for Automatic Particle Counting ofLubricating and Hydraulic Fluids Using Dilution Tech-niques to Eliminate the Contribution of Water and Inter-fering Soft Particles by Light ExtinctionD7690 Practice for Microscopic Characterization of Par-ticles from In-Service Lubricants by Analytical Ferrogra-phyG40 Terminology Relating to Wear and Erosion2.2 ISO Standard:3ISO 11171 Hydraulic fluid power Calibration of automaticparticle counters for liquids3.Terminology3.1 Definitions:3.1.1 abrasive wear,nwear due to hard particles or hardprotuberances forced against and moving along a solid surface.G401This guide is under the jurisdiction of ASTM Committee D02 on PetroleumProducts,Liquid Fuels,and Lubricants and is the direct responsibility of Subcom-mittee D02.96.06 on Practices and Techniques for Prediction and Determination ofMicroscopic Wear and Wear-related Properties.Current edition approved Nov.1,2020.Published December 2020.Originallyapproved in 2011.Last previous edition approved in 2016 as D7684 11(2016).DOI:10.1520/D7684-11R20.2For referenced ASTM standards,visit the ASTM website,www.astm.org,orcontact ASTM Customer Service at serviceastm.org.For Annual Book of ASTMStandards volume information,refer to the standards Document Summary page onthe ASTM website.3Available from International Organization for Standardization(ISO),1,ch.dela Voie-Creuse,Case postale 56,CH-1211,Geneva 20,Switzerland,www.iso.org.Copyright ASTM International,100 Barr Harbor Drive,PO Box C700,West Conshohocken,PA 19428-2959.United StatesThis international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for theDevelopment of International Standards,Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade(TBT)Committee.13.1.2 abrasion,nwear by displacement of material causedby hard particles or hard protuberances.D41753.1.3 break-in,nsee run-in.G403.1.4 fatigue wear,nwear of a

此文档下载收益归作者所有

下载文档
猜你喜欢
你可能关注的文档
收起
展开