温馨提示:
1. 部分包含数学公式或PPT动画的文件,查看预览时可能会显示错乱或异常,文件下载后无此问题,请放心下载。
2. 本文档由用户上传,版权归属用户,汇文网负责整理代发布。如果您对本文档版权有争议请及时联系客服。
3. 下载前请仔细阅读文档内容,确认文档内容符合您的需求后进行下载,若出现内容与标题不符可向本站投诉处理。
4. 下载文档时可能由于网络波动等原因无法下载或下载错误,付费完成后未能成功下载的用户请联系客服处理。
网站客服:3074922707
TM_B_599_
_92_2014
Designation:B59992(Reapproved 2014)Standard Specification forNickel-Iron-Chromium-Molybdenum-Columbium StabilizedAlloy(UNS N08700)Plate,Sheet,and Strip1This standard is issued under the fixed designation B599;the number immediately following the designation indicates the year oforiginal adoption or,in the case of revision,the year of last revision.A number in parentheses indicates the year of last reapproval.Asuperscript epsilon()indicates an editorial change since the last revision or reapproval.1.Scope1.1 Thisspecificationcoversnickel-iron-chromium-molybdenum-columbium stabilized alloy(UNS N08700)2plate,sheet,and strip in the solution-annealed condition.1.2 The values stated in inch-pound units are to be regardedas standard.The values given in parentheses are mathematicalconversions to SI units that are provided for information onlyand are not considered standard.1.3 This standard does not purport to address all of thesafety concerns,if any,associated with its use.It is theresponsibility of the user of this standard to become familiarwith all hazards including those identified in the appropriateMaterial Safety Data Sheet(MSDS)for this product/materialas provided by the manufacturer,to establish appropriatesafety and health practices,and determine the applicability ofregulatory limitations prior to use.2.Referenced Documents2.1 ASTM Standards:3A262 Practices for Detecting Susceptibility to IntergranularAttack in Austenitic Stainless SteelsE8/E8M Test Methods for Tension Testing of Metallic Ma-terialsE10 Test Method for Brinell Hardness of Metallic MaterialsE18 Test Methods for Rockwell Hardness of Metallic Ma-terialsE29 Practice for Using Significant Digits in Test Data toDetermine Conformance with SpecificationsE55 Practice for Sampling Wrought Nonferrous Metals andAlloys for Determination of Chemical CompositionE140 Hardness Conversion Tables for Metals RelationshipAmong Brinell Hardness,Vickers Hardness,RockwellHardness,Superficial Hardness,Knoop Hardness,Sclero-scope Hardness,and Leeb HardnessE350 Test Methods for Chemical Analysis of Carbon Steel,Low-Alloy Steel,Silicon Electrical Steel,Ingot Iron,andWrought IronE353 Test Methods for Chemical Analysis of Stainless,Heat-Resisting,Maraging,and Other Similar Chromium-Nickel-Iron Alloys3.Terminology3.1 Definitions of Terms Specific to This Standard:3.1.1 The terms plate,sheet,and strip as used in thisspecification are described as follows:3.1.2 plate,nmaterial 0.1875 in.(4.76 mm)and over inthickness and over 10 in.(254 mm)in width.3.1.3 sheet,nmaterial under 0.1875 in.(4.76 mm)inthickness and over 24 in.(610 mm)in width.3.1.4 strip,nmaterial under 0.1875 in.(4.76 mm)inthickness and under 24 in.(610 mm)in width.4.Ordering Information4.1 Orders for material under this specification shouldinclude the following information:4.1.1 Quantity(weight or number of pieces).4.1.2 Name of material or UNS N08700.4.1.3 Form(plate,sheet,or strip).4.1.4 Dimensions.4.1.5 Type of edge required(for strip only,see 9.4).4.1.6 Finish(Section 10)For sheet ordered with No.4finish,specify whether one or both sides are to be polished.4.1.7 ASTM designation and year of issue.4.1.8 Corrosion TestState if intergranular corrosion test isrequired(Section 8).4.1.9 MarkingState if metal die identification is requiredon plate14in.(6.35 mm)or thicker(Section 17).4.1.10 Certification or Test ReportsState if certification ortest reports are required(Section 16).1This specification is under the jurisdiction of ASTM Committee B02 onNonferrous Metals and Alloys and is the direct responsibility of SubcommitteeB02.07 on Refined Nickel and Cobalt and Their Alloys.Current edition approved Oct.1,2014.Published October 2014.Originallyapproved in 1980.Last previous edition approved in 2009 as B599 92(2009)1.DOI:10.1520/B0599-92R14.2New designation established in accordance with ASTM E527 and SAE J1086,Practice for Numbering Metals and Alloys(UNS).3For referenced ASTM standards,visit the ASTM website,www.astm.org,orcontact ASTM Customer Service at serviceastm.org.For Annual Book of ASTMStandards volume information,refer to the standards Document Summary page onthe ASTM website.Copyright ASTM International,100 Barr Harbor Drive,PO Box C700,West Conshohocken,PA 19428-2959.United States1 5.Materials and Manufacture5.1 Heat TreatmentThe final heat treatment shall be asolution anneal.Minor cold working such as flattening ortemper rolling may be performed after the final solutionannealing treatment.NOTE1This recommended solution anneal consists of heating to aminimum temperature of 2000F(1090C)and cooling rapidly to roomtemperature.6.Chemical Composition6.1 The material sampled,in accordance with 11.2,shallconform to the composition limits prescribed in Table 1.6.2 If a product analysis is subsequently made,the materialshall conform to the composition limits with the productanalysis variation prescribed in Table 2.7.Mechanical Requirements7.1 The material shall conform to the requirements as to themechanical p